tesa® 4914 Low VOC
Double-sided non-woven tape with differential adhesive
Product Features
- Asymmetrical product design with superior adhesion on liner-covered side
- Excellent performance on rough surfaces like leather and textiles
- Reliable bond, often also on low surface energy surfaces
Product description
tesa® 4914 is a translucent double-sided self-adhesive tape consisting of a non-woven backing and a tackified acrylic adhesive with lower coating weight on the open side.
tesa® 4914 features especially:
- Open side: lower adhesion level
- Easier removal while tearing the bond apart from the original surface even after exposure to demanding environmental conditions
- Covered side: higher adhesion level
- Foamed adhesive coating with high initial tack
- Excellent performance on rough surfaces
Product details and specifications
Product Features
- Asymmetrical product design with superior adhesion on liner-covered side
- Excellent performance on rough surfaces like leather and textiles
- Reliable bond, often also on low surface energy surfaces
- Low VOC according to VDA278 analysis
- Flame retardant according to FAR/JAR/CS 25.853(a) Appendix F part I (a)(1)(ii)
Application Fields
- Mounting of car roof linings in car production
- Lamination of foamed materials in combination with smooth materials on the open side
Product Construction
| Backing material | non-woven |
|---|---|
| Colour | translucent |
| Colour of liner | red |
| Thickness of liner | 80 µm |
| Total thickness | 250 µm |
| Type of adhesive | tackified acrylic |
| Type of liner | PE |
| Weight of liner | 92 g/m² |
Product Construction
| Backing material | non-woven |
|---|---|
| Colour | translucent |
| Colour of liner | red |
| Thickness of liner | 80 µm |
| Total thickness | 250 µm |
| Type of adhesive | tackified acrylic |
| Type of liner | PE |
| Weight of liner | 92 g/m² |
Properties / Performance Values
| Elongation at break | 3 % |
|---|---|
| Tensile strength | 8 N/cm |
| Softener resistance | good |
| Temperature resistance short term duration | 140 °C |
| Static shear resistance | low |
| Ageing resistance (UV) | good |
| Humidity resistance | good |
| Tack | good |
| Chemical resistance | good |
| Minimum temperature resistance | -40 °C |
| Static shear resistance at 40°C | low |
| Temperature resistance long term duration | 80 °C |
| Static shear resistance at 23°C | low |
Properties / Performance Values
| Elongation at break | 3 % |
|---|---|
| Tensile strength | 8 N/cm |
| Softener resistance | good |
| Temperature resistance short term duration | 140 °C |
| Static shear resistance | low |
| Ageing resistance (UV) | good |
| Humidity resistance | good |
| Tack | good |
| Chemical resistance | good |
| Minimum temperature resistance | -40 °C |
| Static shear resistance at 40°C | low |
| Temperature resistance long term duration | 80 °C |
| Static shear resistance at 23°C | low |
Adhesion to Values
| Adhesion to ABS (initial) | 5.6 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 7.7 N/cm |
| Adhesion to ABS (covered side, after 14 days) | 7.6 N/cm |
| Adhesion to ABS (covered side, initial) | 7.6 N/cm |
| Adhesion to Aluminium (initial) | 5.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 6.3 N/cm |
| Adhesion to Alu (covered side, after 14 days) | 8 N/cm |
| Adhesion to Aluminium (covered side, initial) | 7.8 N/cm |
| Adhesion to PC (initial) | 5.8 N/cm |
| Adhesion to PC (after 14 days) | 7.4 N/cm |
| Adhesion to PC (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PC (covered side, initial) | 8.1 N/cm |
| Adhesion to PE (initial) | 3.2 N/cm |
| Adhesion to PE (after 14 days) | 3.4 N/cm |
| Adhesion to PE (covered side, after 14 days) | 5.3 N/cm |
| Adhesion to PE (covered side, initial) | 4.2 N/cm |
| Adhesion to PET (initial) | 4.8 N/cm |
| Adhesion to PET (after 14 days) | 6.2 N/cm |
| Adhesion to PET (covered side, after 14 days) | 7.9 N/cm |
| Adhesion to PET (covered side, initial) | 7.8 N/cm |
| Adhesion to PP (initial) | 4.6 N/cm |
| Adhesion to PP (after 14 days) | 4.4 N/cm |
| Adhesion to PP (covered side, initial) | 5.6 N/cm |
| Adhesion to PP (covered side, after 14 days) | 6.5 N/cm |
| Adhesion to PS (initial) | 5.8 N/cm |
| Adhesion to PS (after 14 days) | 7.4 N/cm |
| Adhesion to PS (covered side, initial) | 8.1 N/cm |
| Adhesion to PS (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PVC (initial) | 4.8 N/cm |
| Adhesion to PVC (after 14 days) | 7.7 N/cm |
| Adhesion to PVC (covered side, after 14 days) | 7.8 N/cm |
| Adhesion to PVC (covered side, initial) | 7.8 N/cm |
| Adhesion to Steel (initial) | 7 N/cm |
| Adhesion to Steel (after 14 days) | 7.8 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 9.3 N/cm |
| Adhesion to Steel (covered side, initial) | 8.2 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 5.6 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 7.7 N/cm |
| Adhesion to ABS (covered side, after 14 days) | 7.6 N/cm |
| Adhesion to ABS (covered side, initial) | 7.6 N/cm |
| Adhesion to Aluminium (initial) | 5.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 6.3 N/cm |
| Adhesion to Alu (covered side, after 14 days) | 8 N/cm |
| Adhesion to Aluminium (covered side, initial) | 7.8 N/cm |
| Adhesion to PC (initial) | 5.8 N/cm |
| Adhesion to PC (after 14 days) | 7.4 N/cm |
| Adhesion to PC (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PC (covered side, initial) | 8.1 N/cm |
| Adhesion to PE (initial) | 3.2 N/cm |
| Adhesion to PE (after 14 days) | 3.4 N/cm |
| Adhesion to PE (covered side, after 14 days) | 5.3 N/cm |
| Adhesion to PE (covered side, initial) | 4.2 N/cm |
| Adhesion to PET (initial) | 4.8 N/cm |
| Adhesion to PET (after 14 days) | 6.2 N/cm |
| Adhesion to PET (covered side, after 14 days) | 7.9 N/cm |
| Adhesion to PET (covered side, initial) | 7.8 N/cm |
| Adhesion to PP (initial) | 4.6 N/cm |
| Adhesion to PP (after 14 days) | 4.4 N/cm |
| Adhesion to PP (covered side, initial) | 5.6 N/cm |
| Adhesion to PP (covered side, after 14 days) | 6.5 N/cm |
| Adhesion to PS (initial) | 5.8 N/cm |
| Adhesion to PS (after 14 days) | 7.4 N/cm |
| Adhesion to PS (covered side, initial) | 8.1 N/cm |
| Adhesion to PS (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PVC (initial) | 4.8 N/cm |
| Adhesion to PVC (after 14 days) | 7.7 N/cm |
| Adhesion to PVC (covered side, after 14 days) | 7.8 N/cm |
| Adhesion to PVC (covered side, initial) | 7.8 N/cm |
| Adhesion to Steel (initial) | 7 N/cm |
| Adhesion to Steel (after 14 days) | 7.8 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 9.3 N/cm |
| Adhesion to Steel (covered side, initial) | 8.2 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.