tesa® 88676 - LSE Filmic Mounting Tape
170µm LSE double-sided transparent PET film tape
Product Features
- Excellent bonding performance with LSE(low surface energy) substrates
- No primer required
- High initial tack at various substrate especially hard-to bond surface
Product description
tesa® 88676 is a high-performance, double-sided transparent PET film tape designed for strong bonding strength on low surface energy (LSE) substrates. With a total thickness of 170µm, coated on both sides with special tackified acrylic adhesive, it can be widely used for various hard-to-bonding substrates without primer, even under demanding environmental conditions.
Product details and specifications
Product Features
- Excellent bonding performance with LSE(low surface energy) substrates
- No primer required
- High initial tack at various substrate especially hard-to bond surface
- Dimensional Stability: PET backing and PE core ensures clean handling and precise die-cuts.
Application Fields
tesa® 88676 is suitable for a wide range of permanent mounting
- Enables primerless adhesion to low surface energy (LSE) substrates such as PP, PE, and EPDM
- Ideal for long-term mounting on hard-to-bond materials, such as foam and gaskets
- Versatile bonding solution for a wide range of demanding industrial application
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Color | transparent |
| Color of liner | white/blue logo |
| Liner Type | PE-coated paper |
| Thickness of liner | 140 µm |
| Total thickness | 170 µm |
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Color | transparent |
| Color of liner | white/blue logo |
| Liner Type | PE-coated paper |
| Thickness of liner | 140 µm |
| Total thickness | 170 µm |
Properties / Performance Values
| Elongation at break | 98 % |
|---|---|
| Tensile strength | 30.2 N/cm |
| Ageing resistance (UV) | good |
| Temperature resistance short term | 150 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term | 95 °C |
| Tack | very good |
Properties / Performance Values
| Elongation at break | 98 % |
|---|---|
| Tensile strength | 30.2 N/cm |
| Ageing resistance (UV) | good |
| Temperature resistance short term | 150 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term | 95 °C |
| Tack | very good |
Adhesion to Values
| Adhesion to ABS (initial) | 14 N/cm |
|---|---|
| Adhesion to ABS (after 3 days) | 14.8 N/cm |
| Adhesion to PE (initial) | 9 N/cm |
| Adhesion to PE (after 3 days) | 9.2 N/cm |
| Adhesion to PP (initial) | 8.8 N/cm |
| Adhesion to PP (after 3 days) | 10.5 N/cm |
| Adhesion to Steel (initial) | 12.5 N/cm |
| Adhesion to Steel (after 3 days) | 14.6 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 14 N/cm |
|---|---|
| Adhesion to ABS (after 3 days) | 14.8 N/cm |
| Adhesion to PE (initial) | 9 N/cm |
| Adhesion to PE (after 3 days) | 9.2 N/cm |
| Adhesion to PP (initial) | 8.8 N/cm |
| Adhesion to PP (after 3 days) | 10.5 N/cm |
| Adhesion to Steel (initial) | 12.5 N/cm |
| Adhesion to Steel (after 3 days) | 14.6 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.