tesa® 6917
Filmic double-sided bag sealing tape with differential adhesive
Product Features
- Due to different adhesion values on each side, tesa® 6917 offers good removability on the covered adhesive side.
- tesa® 6917 comes with fingerlift (extended liner) for conveniant liner removal.
Product description
tesa® 6917 has been designed for re-sealable filmic bags. It consists of a transparent double-sided PP-film with a differential adhesive system. The product can easily be cut with the hot wire systems of common bag machine producers.
Product details and specifications
Product Features
- Due to different adhesion values on each side, tesa® 6917 offers good removability on the covered adhesive side.
- tesa® 6917 comes with fingerlift (extended liner) for conveniant liner removal.
Application Fields
- Reopenable closure system for filmic bags
- Removable emblems or profiles
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Backing material | PP film |
| Color | transparent |
| Color of liner | red |
| Liner Type | MOPP |
| Thickness of liner | 80 µm |
| Total thickness | 90 µm |
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Backing material | PP film |
| Color | transparent |
| Color of liner | red |
| Liner Type | MOPP |
| Thickness of liner | 80 µm |
| Total thickness | 90 µm |
Properties / Performance Values
| Elongation at break | 150 % |
|---|---|
| Tack | good |
| Static shear resistance at 40°C | good |
| Humidity resistance | very good |
| Ageing resistance (UV) | very good |
| Chemical Resistance | good |
| Temperature resistance short term | 120 °C |
| Temperature resistance long term | 80 °C |
| Softener resistance | medium |
| Static shear resistance at 23°C | good |
Properties / Performance Values
| Elongation at break | 150 % |
|---|---|
| Tack | good |
| Static shear resistance at 40°C | good |
| Humidity resistance | very good |
| Ageing resistance (UV) | very good |
| Chemical Resistance | good |
| Temperature resistance short term | 120 °C |
| Temperature resistance long term | 80 °C |
| Softener resistance | medium |
| Static shear resistance at 23°C | good |
Adhesion to Values
| Adhesion to ABS (initial) | 6.9 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 10.1 N/cm |
| Adhesion to ABS (covered side, initial) | 4.2 N/cm |
| Adhesion to ABS (covered side, after 14 days) | 6 N/cm |
| Adhesion to Aluminium (initial) | 7.7 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.2 N/cm |
| Adhesion to Aluminium (covered side, after 14 days) | 4.7 N/cm |
| Adhesion to Aluminium (covered side, initial) | 3.5 N/cm |
| Adhesion to PC (initial) | 9 N/cm |
| Adhesion to PC (after 14 days) | 11 N/cm |
| Adhesion to PC (covered side, after 14 days) | 6.8 N/cm |
| Adhesion to PC (covered side, initial) | 4 N/cm |
| Adhesion to PE (initial) | 3.9 N/cm |
| Adhesion to PE (after 14 days) | 4.1 N/cm |
| Adhesion to PE (covered side, after 14 days) | 2.3 N/cm |
| Adhesion to PE (covered side, initial) | 1.6 N/cm |
| Adhesion to PET (initial) | 6.6 N/cm |
| Adhesion to PET (after 14 days) | 9.3 N/cm |
| Adhesion to PET (covered side, after 14 days) | 4.7 N/cm |
| Adhesion to PET (covered side, initial) | 3.1 N/cm |
| Adhesion to PP (initial) | 3.8 N/cm |
| Adhesion to PP (after 14 days) | 6.9 N/cm |
| Adhesion to PP (covered side, initial) | 1.9 N/cm |
| Adhesion to PP (covered side, after 14 days) | 2.6 N/cm |
| Adhesion to PS (initial) | 7.9 N/cm |
| Adhesion to PS (after 14 days) | 10 N/cm |
| Adhesion to PS (covered side, after 14 days) | 5.6 N/cm |
| Adhesion to PS (covered side, initial) | 3.8 N/cm |
| Adhesion to PVC (initial) | 6.5 N/cm |
| Adhesion to PVC (after 14 days) | 11 N/cm |
| Adhesion to PVC (covered side, initial) | 4 N/cm |
| Adhesion to PVC (covered side, after 14 days) | 7 N/cm |
| Adhesion to Steel (initial) | 8.2 N/cm |
| Adhesion to Steel (after 14 days) | 11.4 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 4.1 N/cm |
| Adhesion to Steel (covered side, initial) | 4.5 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 6.9 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 10.1 N/cm |
| Adhesion to ABS (covered side, initial) | 4.2 N/cm |
| Adhesion to ABS (covered side, after 14 days) | 6 N/cm |
| Adhesion to Aluminium (initial) | 7.7 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.2 N/cm |
| Adhesion to Aluminium (covered side, after 14 days) | 4.7 N/cm |
| Adhesion to Aluminium (covered side, initial) | 3.5 N/cm |
| Adhesion to PC (initial) | 9 N/cm |
| Adhesion to PC (after 14 days) | 11 N/cm |
| Adhesion to PC (covered side, after 14 days) | 6.8 N/cm |
| Adhesion to PC (covered side, initial) | 4 N/cm |
| Adhesion to PE (initial) | 3.9 N/cm |
| Adhesion to PE (after 14 days) | 4.1 N/cm |
| Adhesion to PE (covered side, after 14 days) | 2.3 N/cm |
| Adhesion to PE (covered side, initial) | 1.6 N/cm |
| Adhesion to PET (initial) | 6.6 N/cm |
| Adhesion to PET (after 14 days) | 9.3 N/cm |
| Adhesion to PET (covered side, after 14 days) | 4.7 N/cm |
| Adhesion to PET (covered side, initial) | 3.1 N/cm |
| Adhesion to PP (initial) | 3.8 N/cm |
| Adhesion to PP (after 14 days) | 6.9 N/cm |
| Adhesion to PP (covered side, initial) | 1.9 N/cm |
| Adhesion to PP (covered side, after 14 days) | 2.6 N/cm |
| Adhesion to PS (initial) | 7.9 N/cm |
| Adhesion to PS (after 14 days) | 10 N/cm |
| Adhesion to PS (covered side, after 14 days) | 5.6 N/cm |
| Adhesion to PS (covered side, initial) | 3.8 N/cm |
| Adhesion to PVC (initial) | 6.5 N/cm |
| Adhesion to PVC (after 14 days) | 11 N/cm |
| Adhesion to PVC (covered side, initial) | 4 N/cm |
| Adhesion to PVC (covered side, after 14 days) | 7 N/cm |
| Adhesion to Steel (initial) | 8.2 N/cm |
| Adhesion to Steel (after 14 days) | 11.4 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 4.1 N/cm |
| Adhesion to Steel (covered side, initial) | 4.5 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.