tesa® 88663
150µm double coated PET tape
Product Features
- Excellent adhesion to a wide variety surfaces
- Great shear strength
- Great temperature resistance
Product description
tesa® 88663 is a transparent, double coated self-adhesive tape consisting of a PET backing and a tackified acrylic adhesive specifically designed for Industrial Trade & Converting market. It is the ideal solution for multi-purpose laminating and converting applications.
Product details and specifications
Product Features
- Excellent adhesion to a wide variety surfaces
- Great shear strength
- Great temperature resistance
- Toluene-free adhesive
- Humidity resistant PE-coated liner
Application Fields
- Foam lamination
- Light strips mounting
- Name plate mounting
- Mylar film mounting
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Backing material | PET |
| Color | transparent |
| Color of liner | white/blue logo |
| Liner Type | PE-coated paper |
| Thickness of liner | 140 µm |
| Total thickness | 150 µm |
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Backing material | PET |
| Color | transparent |
| Color of liner | white/blue logo |
| Liner Type | PE-coated paper |
| Thickness of liner | 140 µm |
| Total thickness | 150 µm |
Properties / Performance Values
| Elongation at break | 50 % |
|---|---|
| Tensile strength | 40 N/cm |
| Temperature resistance short term | 200 °C |
| Static shear resistance at 23°C | very good |
| Tack | medium |
| Static shear resistance at 70°C | good |
| Temperature resistance long term | 95 °C |
Properties / Performance Values
| Elongation at break | 50 % |
|---|---|
| Tensile strength | 40 N/cm |
| Temperature resistance short term | 200 °C |
| Static shear resistance at 23°C | very good |
| Tack | medium |
| Static shear resistance at 70°C | good |
| Temperature resistance long term | 95 °C |
Adhesion to Values
| Adhesion to ABS (initial) | 11 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 13.2 N/cm |
| Adhesion to PC (initial) | 11.1 N/cm |
| Adhesion to PC (after 14 days) | 15.3 N/cm |
| Adhesion to PE (initial) | 4.6 N/cm |
| Adhesion to PE (after 14 days) | 5.2 N/cm |
| Adhesion to PET (initial) | 11.3 N/cm |
| Adhesion to PET (after 14 days) | 12.9 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 5.3 N/cm |
| Adhesion to Steel (initial) | 11.6 N/cm |
| Adhesion to Steel (after 14 days) | 13.8 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 11 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 13.2 N/cm |
| Adhesion to PC (initial) | 11.1 N/cm |
| Adhesion to PC (after 14 days) | 15.3 N/cm |
| Adhesion to PE (initial) | 4.6 N/cm |
| Adhesion to PE (after 14 days) | 5.2 N/cm |
| Adhesion to PET (initial) | 11.3 N/cm |
| Adhesion to PET (after 14 days) | 12.9 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 5.3 N/cm |
| Adhesion to Steel (initial) | 11.6 N/cm |
| Adhesion to Steel (after 14 days) | 13.8 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.