Product Construction
Backing material | PE extruded cloth |
Thickness of tape | _NULL µm |
Total thickness | 125 µm |
Type of adhesive | type: acrylic |
Multipurpose outdoor cloth tape
tesa® 4621 is a translucent green pressure sensitive adhesive tape based on an acrylic adhesive and a polyethylene backing reinforced with a polyester cloth.
.
Backing material | PE extruded cloth |
Thickness of tape | _NULL µm |
Total thickness | 125 µm |
Type of adhesive | type: acrylic |
Backing material | PE extruded cloth |
Thickness of tape | _NULL µm |
Total thickness | 125 µm |
Type of adhesive | type: acrylic |
Easy to remove | yes |
Suitable for die cutting | yes |
Abrasion resistance | medium |
Temperature resistance (30 min) | 95 °C |
UV resistance | 8 week/s |
Elongation at break | 22 % |
Tensile strength | 54 N/cm |
Unwind force n/cm | 1.2 N/cm |
Residue free removal | yes |
Easy to write on | yes |
Tack | very good |
Straight tear edges | good, medium |
Ageing resistance (UV) | very good |
Mesh | 100 threads/inch² |
Hand tearability | very good |
Temperature resistance (removability from aluminum after 30 min exposure) | 95 °C |
Water resistance | good, medium |
Easy to remove | yes |
Suitable for die cutting | yes |
Abrasion resistance | medium |
Temperature resistance (30 min) | 95 °C |
UV resistance | 8 week/s |
Elongation at break | 22 % |
Tensile strength | 54 N/cm |
Unwind force n/cm | 1.2 N/cm |
Residue free removal | yes |
Easy to write on | yes |
Tack | very good |
Straight tear edges | good, medium |
Ageing resistance (UV) | very good |
Mesh | 100 threads/inch² |
Hand tearability | very good |
Temperature resistance (removability from aluminum after 30 min exposure) | 95 °C |
Water resistance | good, medium |
Adhesion to Glass (initial) | 2.7 N/cm |
Adhesion to PE (initial) | 1.1 N/cm |
Adhesion to Steel | 2.6 N/cm |
Adhesion to Glass (initial) | 2.7 N/cm |
Adhesion to PE (initial) | 1.1 N/cm |
Adhesion to Steel | 2.6 N/cm |