Additional Info
Liner variants:
PV0 brown glassine paper (71µm; 82g/m²)
PV6 red MOPP-film (80µm; 72g/m²)
PV0 brown glassine paper (71µm; 82g/m²)
PV6 red MOPP-film (80µm; 72g/m²)
Double-sided strong lamination filmic tape
tesa® 4982 is a transparent double-sided self-adhesive tape consisting of a PET backing and a modified acrylic adhesive.
tesa® 4982 features especially:
| Backing material | PET film |
|---|---|
| Colour | transparent |
| Total thickness | 100 µm |
| Type of adhesive | tackified acrylic |
| Backing material | PET film |
|---|---|
| Colour | transparent |
| Total thickness | 100 µm |
| Type of adhesive | tackified acrylic |
| Elongation at break | 50 % |
|---|---|
| Tensile strength | 20 N/cm |
| Temperature resistance short term duration | 200 °C |
| Static shear resistance at 40°C | very good |
| Ageing resistance (UV) | good |
| Temperature resistance long term duration | 100 °C |
| Tack | good |
| Humidity resistance | very good |
| Static shear resistance at 23°C | very good |
| Softener resistance | good |
| Elongation at break | 50 % |
|---|---|
| Tensile strength | 20 N/cm |
| Temperature resistance short term duration | 200 °C |
| Static shear resistance at 40°C | very good |
| Ageing resistance (UV) | good |
| Temperature resistance long term duration | 100 °C |
| Tack | good |
| Humidity resistance | very good |
| Static shear resistance at 23°C | very good |
| Softener resistance | good |
| Adhesion to ABS (initial) | 7.6 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 9.6 N/cm |
| Adhesion to Aluminium (initial) | 7.9 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
| Adhesion to PC (initial) | 9.2 N/cm |
| Adhesion to PC (after 14 days) | 11 N/cm |
| Adhesion to PE (initial) | 4.6 N/cm |
| Adhesion to PE (after 14 days) | 5.1 N/cm |
| Adhesion to PET (initial) | 7 N/cm |
| Adhesion to PET (after 14 days) | 8.4 N/cm |
| Adhesion to PP (initial) | 4.4 N/cm |
| Adhesion to PP (after 14 days) | 6.2 N/cm |
| Adhesion to PS (initial) | 8.3 N/cm |
| Adhesion to PS (after 14 days) | 9.2 N/cm |
| Adhesion to PVC (initial) | 7 N/cm |
| Adhesion to PVC (after 14 days) | 10 N/cm |
| Adhesion to Steel (initial) | 11 N/cm |
| Adhesion to Steel (after 14 days) | 11.7 N/cm |
| Adhesion to ABS (initial) | 7.6 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 9.6 N/cm |
| Adhesion to Aluminium (initial) | 7.9 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
| Adhesion to PC (initial) | 9.2 N/cm |
| Adhesion to PC (after 14 days) | 11 N/cm |
| Adhesion to PE (initial) | 4.6 N/cm |
| Adhesion to PE (after 14 days) | 5.1 N/cm |
| Adhesion to PET (initial) | 7 N/cm |
| Adhesion to PET (after 14 days) | 8.4 N/cm |
| Adhesion to PP (initial) | 4.4 N/cm |
| Adhesion to PP (after 14 days) | 6.2 N/cm |
| Adhesion to PS (initial) | 8.3 N/cm |
| Adhesion to PS (after 14 days) | 9.2 N/cm |
| Adhesion to PVC (initial) | 7 N/cm |
| Adhesion to PVC (after 14 days) | 10 N/cm |
| Adhesion to Steel (initial) | 11 N/cm |
| Adhesion to Steel (after 14 days) | 11.7 N/cm |
Download the files below for more technical details and information on this product.