tesa® 62510

1000 µm double sided PE foam tape

Product Features

High ultimate adhesion level for a reliable bonding performance
Skin contact certification according to ISO 10993-5 and ISO 10993-10
Fully outdoor suitable: UV, water and ageing resistant

All product features

Product description

tesa® 62510 is a double sided PE foam tape for mounting applications. It consists of a highly conformable PE foam backing and a tackified acrylic adhesive.

Product details and specifications

Product Features

High ultimate adhesion level for a reliable bonding performance
Skin contact certification according to ISO 10993-5 and ISO 10993-10
Fully outdoor suitable: UV, water and ageing resistant
Conformable PE foam core with high inner strength
Suitable for automatic and manual module assembly
Easy solar module assembly due to a high foam compression rate

Application Fields

General mounting applications
Mounting of trims and profiles
Solar module frames

Adhesive Type	tackified acrylic
Backing material	PE foam
Color	black/white
Total thickness	1,000 µm

Adhesive Type	tackified acrylic
Backing material	PE foam
Color	black/white
Total thickness	1,000 µm

Elongation at break	180 %
Tensile strength	10 N/cm
Humidity resistance	very good
Static shear resistance at 40°C	good
Tack	good
Static shear resistance at 70°C	very good
Temperature resistance long term	80 °C
Ageing resistance (UV)	very good
Softener resistance	medium
Static shear resistance at 23°C	good
Temperature resistance short term	80 °C

Elongation at break	180 %
Tensile strength	10 N/cm
Humidity resistance	very good
Static shear resistance at 40°C	good
Tack	good
Static shear resistance at 70°C	very good
Temperature resistance long term	80 °C
Ageing resistance (UV)	very good
Softener resistance	medium
Static shear resistance at 23°C	good
Temperature resistance short term	80 °C

Adhesion to ABS (initial)	8 N/cm
Adhesion to ABS (after 14 days)	13.5 N/cm
Adhesion to Aluminium (initial)	8 N/cm
Adhesion to Aluminium (after 14 days)	13.5 N/cm
Adhesion to PC (initial)	8 N/cm
Adhesion to PC (after 14 days)	13.5 N/cm
Adhesion to PE (initial)	0.9 N/cm
Adhesion to PE (after 14 days)	0.9 N/cm
Adhesion to PET (initial)	6 N/cm
Adhesion to PET (after 14 days)	13.5 N/cm
Adhesion to PP (initial)	1.2 N/cm
Adhesion to PP (after 14 days)	1.2 N/cm
Adhesion to PS (initial)	8 N/cm
Adhesion to PS (after 14 days)	8 N/cm
Adhesion to PVC (initial)	13.5 N/cm
Adhesion to PVC (after 14 days)	13.5 N/cm
Adhesion to Steel (initial)	13.5 N/cm
Adhesion to Steel (after 14 days)	13.5 N/cm

Adhesion to ABS (initial)	8 N/cm
Adhesion to ABS (after 14 days)	13.5 N/cm
Adhesion to Aluminium (initial)	8 N/cm
Adhesion to Aluminium (after 14 days)	13.5 N/cm
Adhesion to PC (initial)	8 N/cm
Adhesion to PC (after 14 days)	13.5 N/cm
Adhesion to PE (initial)	0.9 N/cm
Adhesion to PE (after 14 days)	0.9 N/cm
Adhesion to PET (initial)	6 N/cm
Adhesion to PET (after 14 days)	13.5 N/cm
Adhesion to PP (initial)	1.2 N/cm
Adhesion to PP (after 14 days)	1.2 N/cm
Adhesion to PS (initial)	8 N/cm
Adhesion to PS (after 14 days)	8 N/cm
Adhesion to PVC (initial)	13.5 N/cm
Adhesion to PVC (after 14 days)	13.5 N/cm
Adhesion to Steel (initial)	13.5 N/cm
Adhesion to Steel (after 14 days)	13.5 N/cm

Liner variants:

PV0 brown glassine paper (71 µm)
PV13 transparent PET film (50 µm)
PV15 blue PE film (100 µm)

Peel Adhesion:

immediately: foam splitting on steel
after 14 days: foam splitting on steel, ABS, Aluminum, PC, PET, PS, PVC

tesa® 62510 is recognized by UL as photovoltaic polymeric material (QIHE2).

tesa® 62510 has been tested by TÜV Rheinland, Germany. The test confirms the longterm adhesion performance after IEC 61215 climate tests and a 85°C temperature resistance.

The temperature resistance (short/long) of tesa® 62510 has been approved according to tesa test method under static load.

tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.

Downloads

Download the files below for more technical details and information on this product.

Safety data sheet_tesa® 62510_en_en-US_v10 131.1 kB tesa 625xx Family Skin contact - statement 124.4 kB Product information_tesa® 62510_en 54 kB

Contact us

Thank you for your message

We'll get back to you as soon as possible.

Best regards

Your tesa Team

Something went wrong. Please try again later.

Product comparison

Name of product	tesa® 62510	tesa® 6308 New Bond	tesa® 6305 New Bond	tesa® 6311 New Bond	tesa® 67006 New Bond	tesa® 67008 New Bond	tesa® flameXtinct 45001	tesa® 63608	tesa® 63605	tesa® 88623	tesa® 67004 New Bond	tesa® 63615
Total thickness	1,000 µm	800 µm	500 µm	1,100 µm	640 µm	800 µm	1,000 µm	800 µm	500 µm	1,000 µm	400 µm	1,500 µm
Adhesive Type	tackified acrylic	LSE	LSE	LSE	modified acrylic	modified acrylic	FR acrylic	tackified acrylic	tackified acrylic	tackified acrylic	modified acrylic	tackified acrylic
Backing material	PE foam	Acrylic foam	Acrylic foam	Acrylic foam	Acrylic foam	Acrylic foam	FR PE foam	PE foam	PE foam	PE foam	Acrylic foam	PE foam
Color	black/white	gray	gray	gray	gray	gray	white	black/white	black/white	white	gray	black/white
Adhesion to Steel (initial)	13.5 N/cm	28 N/cm	26 N/cm	30 N/cm		17 N/cm	19.2 N/cm	11 N/cm	12 N/cm	22 N/cm	14 N/cm	12 N/cm
Adhesion to Steel (after 14 days)	13.5 N/cm						22 N/cm	11 N/cm	12 N/cm			12 N/cm
Adhesion to PVC (initial)	13.5 N/cm							5 N/cm	5 N/cm	13 N/cm		6 N/cm