tesa® 70410 Bond & Detach
100µm double-sided white Bond & Detach tape
Sustainable Aspects
- solvent free coating
- Thickness: 100µm
- Very high bonding strength
- Superior push out and shock resistance
Product description
tesa® 70410 is a double-sided mounting tape which can be removed by stretching the adhesive in the bond plane (stripping).
Product details and specifications
Product Features
- Thickness: 100µm
- Very high bonding strength
- Superior push out and shock resistance
- Easy removability even after long bonding time by stretching the adhesive
Application Fields
- Temporary fixation of components in electronic devices during the production process
- Permanent mounting of components in electronic devices with the option to remove the parts for repairing or recycling
Sustainable Aspects
- solvent free coating
Product Construction
| Adhesive Type | specialty |
|---|---|
| Backing material | none |
| Color | white |
| Color of liner | brown |
| Liner Type | glassine |
| Thickness of liner | 72 µm |
| Total thickness | 100 µm |
Product Construction
| Adhesive Type | specialty |
|---|---|
| Backing material | none |
| Color | white |
| Color of liner | brown |
| Liner Type | glassine |
| Thickness of liner | 72 µm |
| Total thickness | 100 µm |
Properties / Performance Values
| Static shear resistance at 23°C | very good |
|---|---|
| Solvent free | yes |
| Static shear resistance at 40°C | very good |
| Removability after 14 days (23°C) | very good |
| Temperature resistance long term | 60 °C |
| Temperature resistance short term | 90 °C |
| Residue-free removability | yes |
Properties / Performance Values
| Static shear resistance at 23°C | very good |
|---|---|
| Solvent free | yes |
| Static shear resistance at 40°C | very good |
| Removability after 14 days (23°C) | very good |
| Temperature resistance long term | 60 °C |
| Temperature resistance short term | 90 °C |
| Residue-free removability | yes |
Adhesion to Values
| Adhesion to Aluminium (initial) | 9 N/cm |
|---|---|
| Adhesion to Aluminium (after 14 days) | 9 N/cm |
| Adhesion to Magnesium (initial) | 8 N/cm |
| Adhesion to Magnesium (after 14 days) | 8 N/cm |
| Adhesion to PE (initial) | 8 N/cm |
| Adhesion to PE (after 14 days) | 8 N/cm |
| Adhesion to Steel (initial) | 11 N/cm |
| Adhesion to Steel (after 14 days) | 11 N/cm |
Adhesion to Values
| Adhesion to Aluminium (initial) | 9 N/cm |
|---|---|
| Adhesion to Aluminium (after 14 days) | 9 N/cm |
| Adhesion to Magnesium (initial) | 8 N/cm |
| Adhesion to Magnesium (after 14 days) | 8 N/cm |
| Adhesion to PE (initial) | 8 N/cm |
| Adhesion to PE (after 14 days) | 8 N/cm |
| Adhesion to Steel (initial) | 11 N/cm |
| Adhesion to Steel (after 14 days) | 11 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.