tesa® 68503
30µm double-sided transparent filmic tape
Product Features
- Thickness: 30μm
- Good adhesion level
- Very smooth appearance
Product description
tesa® 68503 is a transparent, double-sided self-adhesive tape consisting of a PET backing, a tackified acrylic adhesive and double PET liner.
Due to the very smooth and excellent appearance it is the perfect solution for display applications.
Product details and specifications
Product Features
- Thickness: 30μm
- Good adhesion level
- Very smooth appearance
- Excellent resistance to demanding environmental conditions
- Excellent handling performance in converting processes
- Double PET liner (36µm easy-release inside / 50µm tight-release outside)
Application Fields
- Force touch film bonding
- FPC and PCB mounting
- LED light bar fixation
- Reflector and optical sheet fixation
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Backing material | PET film |
| Color | transparent |
| Liner Type | PET film |
| Thickness of liner - inside | 36 µm |
| Thickness of liner - outside | 50 µm |
| Total thickness | 30 µm |
| Type of liner - inside | PET |
| Type of liner - outside | PET |
Product Construction
| Adhesive Type | tackified acrylic |
|---|---|
| Backing material | PET film |
| Color | transparent |
| Liner Type | PET film |
| Thickness of liner - inside | 36 µm |
| Thickness of liner - outside | 50 µm |
| Total thickness | 30 µm |
| Type of liner - inside | PET |
| Type of liner - outside | PET |
Properties / Performance Values
| Ageing resistance (UV) | very good |
|---|---|
| Chemical Resistance | good |
| Tack | low |
| Static shear resistance at 23°C | good |
| Softener resistance | good |
| Temperature resistance short term | 200 °C |
| Humidity resistance | very good |
| Temperature resistance long term | 100 °C |
| Static shear resistance at 40°C | good |
Properties / Performance Values
| Ageing resistance (UV) | very good |
|---|---|
| Chemical Resistance | good |
| Tack | low |
| Static shear resistance at 23°C | good |
| Softener resistance | good |
| Temperature resistance short term | 200 °C |
| Humidity resistance | very good |
| Temperature resistance long term | 100 °C |
| Static shear resistance at 40°C | good |
Adhesion to Values
| Adhesion to PC (initial) | 8.5 N/cm |
|---|---|
| Adhesion to PC (after 14 days) | 8.9 N/cm |
| Adhesion to PC (covered side, initial) | 8 N/cm |
| Adhesion to PC (covered side, after 14 days) | 8.5 N/cm |
| Adhesion to PE (initial) | 4.2 N/cm |
| Adhesion to PE (after 14 days) | 4.7 N/cm |
| Adhesion to PE (covered side, initial) | 4.2 N/cm |
| Adhesion to PE (covered side, after 14 days) | 4.7 N/cm |
| Adhesion to PET (initial) | 6.2 N/cm |
| Adhesion to PET (after 14 days) | 6.6 N/cm |
| Adhesion to PET (covered side, after 14 days) | 6.4 N/cm |
| Adhesion to PET (covered side, initial) | 6.3 N/cm |
| Adhesion to PI (initial) | 7.9 N/cm |
| Adhesion to PI (after 14 days) | 8 N/cm |
| Adhesion to PI (covered side, initial) | 7.9 N/cm |
| Adhesion to PI (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PMMA (initial) | 8.2 N/cm |
| Adhesion to PMMA (after 14 days) | 8.2 N/cm |
| Adhesion to PMMA (covered side, after 14 days) | 8.4 N/cm |
| Adhesion to PMMA (covered side, initial) | 8.3 N/cm |
| Adhesion to Steel (initial) | 7.2 N/cm |
| Adhesion to Steel (after 14 days) | 8.1 N/cm |
| Adhesion to Steel (covered side, initial) | 7.7 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 8.3 N/cm |
Adhesion to Values
| Adhesion to PC (initial) | 8.5 N/cm |
|---|---|
| Adhesion to PC (after 14 days) | 8.9 N/cm |
| Adhesion to PC (covered side, initial) | 8 N/cm |
| Adhesion to PC (covered side, after 14 days) | 8.5 N/cm |
| Adhesion to PE (initial) | 4.2 N/cm |
| Adhesion to PE (after 14 days) | 4.7 N/cm |
| Adhesion to PE (covered side, initial) | 4.2 N/cm |
| Adhesion to PE (covered side, after 14 days) | 4.7 N/cm |
| Adhesion to PET (initial) | 6.2 N/cm |
| Adhesion to PET (after 14 days) | 6.6 N/cm |
| Adhesion to PET (covered side, after 14 days) | 6.4 N/cm |
| Adhesion to PET (covered side, initial) | 6.3 N/cm |
| Adhesion to PI (initial) | 7.9 N/cm |
| Adhesion to PI (after 14 days) | 8 N/cm |
| Adhesion to PI (covered side, initial) | 7.9 N/cm |
| Adhesion to PI (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PMMA (initial) | 8.2 N/cm |
| Adhesion to PMMA (after 14 days) | 8.2 N/cm |
| Adhesion to PMMA (covered side, after 14 days) | 8.4 N/cm |
| Adhesion to PMMA (covered side, initial) | 8.3 N/cm |
| Adhesion to Steel (initial) | 7.2 N/cm |
| Adhesion to Steel (after 14 days) | 8.1 N/cm |
| Adhesion to Steel (covered side, initial) | 7.7 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 8.3 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.