Product Construction
Backing material | none |
Color | transparent |
Color of liner | yellow |
Thickness of liner | 80 µm |
Thickness of tape | 100 µm |
Type of adhesive | type: water-based acrylic |
Type of liner | type: glassine |
100 µm double sided transfer tape for lamination and converting applications
tesa® 52110 is a conformable transfer tape, equipped with a water-based acrylic adhesive and a thickness of 100 µm. The water-based acrylic adhesive is temperature resistant up to 180°C and offers very good bonding strength on various substrates. tesa® 52110 was specifically developed for all kinds of lamination and converting applications. Due to its low emission values, it is classified as ultra low VOC and particularly suited to meet interior requirements, e.g. in the automotive industry.
tesa® 52110 is available in efficient laminating lengths and widths as well as in a 50 µm version (tesa® 52105).
Backing material | none |
Color | transparent |
Color of liner | yellow |
Thickness of liner | 80 µm |
Thickness of tape | 100 µm |
Type of adhesive | type: water-based acrylic |
Type of liner | type: glassine |
Backing material | none |
Color | transparent |
Color of liner | yellow |
Thickness of liner | 80 µm |
Thickness of tape | 100 µm |
Type of adhesive | type: water-based acrylic |
Type of liner | type: glassine |
Temperature resistance short term | 100 °C |
Humidity resistance | good |
Ageing resistance (UV) | very good |
Suitable for rough surfaces | very good |
Fogging | very good |
Temperature resistance max. | 180 °C |
Temperature resistance short term | 100 °C |
Humidity resistance | good |
Ageing resistance (UV) | very good |
Suitable for rough surfaces | very good |
Fogging | very good |
Temperature resistance max. | 180 °C |
Adhesion to PP (initial) | 5.1 N/cm |
Adhesion to PP (after 14 days) | 6.8 N/cm |
Adhesion to Steel (initial) | 9.2 N/cm |
Adhesion to Steel (after 14 days) | 11.6 N/cm |
Adhesion to PP (initial) | 5.1 N/cm |
Adhesion to PP (after 14 days) | 6.8 N/cm |
Adhesion to Steel (initial) | 9.2 N/cm |
Adhesion to Steel (after 14 days) | 11.6 N/cm |