tesa® 6965 - Team 4965 Fingerlift
Double-sided filmic tape with fingerlift
Product Features
- Fast liner removal due to fingerlift
- High initial adhesion for fast closure
- Recycling friendly according to the INGEDE method
Product description
tesa® 6965 consists of a transparent PET-film and an adhesive system that combines good adhesion with high shear resistance. It is especially resistant to plasticisers and offers a secure bond even at elevated temperatures.
Product details and specifications
Product Features
- Fast liner removal due to fingerlift
- High initial adhesion for fast closure
- Recycling friendly according to the INGEDE method
- Skin contact certification according to ISO 10993-5 and ISO 10993-10
- Immediate usability right after assembly
- Reliable bonding performance even at high temperatures and on rough corrugated-board surfaces
- Low VOC – measured according to VDA 278 analysis
Application Fields
- Mounting of ABS plastic parts in the car industry
- Mounting of rubber/EPDM profiles
- Mounting of decorative profiles and mouldings in the furniture industry
- Closure of cardboard boxes
| Backing material | PET film |
|---|---|
| Colour | transparent |
| Total thickness | 205 µm |
| Type of adhesive | tackified acrylic |
| Elongation at break | 50 % |
|---|---|
| Tensile strength | 20 N/cm |
| Chemical resistance | good |
| Temperature resistance long term duration | 100 °C |
| Humidity resistance | very good |
| Temperature resistance short term duration | 200 °C |
| Minimum temperature resistance | -40 °C |
| Tack | good |
| Softener resistance | good |
| Static shear resistance at 40°C | very good |
| Ageing resistance (UV) | good |
| Static shear resistance at 23°C | very good |
| Adhesion to ABS (initial) | 10.3 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 12 N/cm |
| Adhesion to Aluminium (initial) | 9.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
| Adhesion to PC (initial) | 12.6 N/cm |
| Adhesion to PC (after 14 days) | 14 N/cm |
| Adhesion to PE (initial) | 5.8 N/cm |
| Adhesion to PE (after 14 days) | 6.9 N/cm |
| Adhesion to PET (initial) | 9.2 N/cm |
| Adhesion to PET (after 14 days) | 9.5 N/cm |
| Adhesion to PP (initial) | 6.8 N/cm |
| Adhesion to PP (after 14 days) | 7.9 N/cm |
| Adhesion to PS (initial) | 10.6 N/cm |
| Adhesion to PS (after 14 days) | 12 N/cm |
| Adhesion to PVC (initial) | 8.7 N/cm |
| Adhesion to PVC (after 14 days) | 13 N/cm |
| Adhesion to Steel (initial) | 11.5 N/cm |
| Adhesion to Steel (after 14 days) | 11.8 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.
Downloads
Download the files below for more technical details and information on this product.
Contact us
Product comparison
Last updated on 24 Aug 2026