tesa^® 68942

Name: tesa® 68942
Brand: tesa®

50µm double sided white filmic tape

Product description

tesa^® 68942 is a white, double-sided self-adhesive tape consisting of a white PET backing and a tackified acrylic adhesive.

tesa^® 68942 features esp.

Thickness: 50µm
High adhesion level
White color for easy detection or design purpose
High resistance to demanding environmental conditions
Good handling performance in converting processes

Main applications

tesa^® 68942 is used for general mounting and laminating applications especially in the electronics industry.

Technical properties

Backing material

PET film

Color

white

Total thickness

50 µm

Type of adhesive

tackified acrylic

Elongation at break

50 %

Tensile strength

20 N/cm

Adhesion properties

Adhesion to ABS (after 14 days)

6.1 N/cm

Adhesion to ABS (initial)

5 N/cm

Adhesion to Aluminium (after 14 days)

6 N/cm

Adhesion to Aluminium (initial)

5 N/cm

Adhesion to PC (after 14 days)

6.4 N/cm

Adhesion to PC (initial)

5.3 N/cm

Adhesion to Steel (after 14 days)

7.3 N/cm

Adhesion to Steel (initial)

5.5 N/cm

Rating properties

Temperature resistance short term

200 °C

Temperature resistance long term

100 °C

Tack

Ageing resistance (UV)

Humidity resistance

Softener resistance

Static shear resistance at 23°C

tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.