Product Construction
| Adhesive Type | nitrile rubber / phenolic resin |
| Backing material | none |
| Color | amber |
| Liner Type | glassine |
| Total thickness | 10.63 mils
270 µm |
tesa HAF® 8400
270µm amber reactive HAF mounting tape
Product description
tesa HAF® 8400 is a reactive heat activated film based on phenolic resin and nitrile rubber. This amber double sided tape has no backing. It is protected by a strong paper liner and can easily be slit and die cut.
At room temperature tesa HAF® 8400 is not tacky. It is activated for pre-lamination by heat and starts to become tacky at 90 °C/194° F. In a second application step heat and pressure is applied over a certain period of time.
After curing tesa HAF® 8400 reaches:
- Very high bonding strength
- High temperature resistance
- Excellent chemical resistance
- Bonds remain flexible and elastic
Product details and specifications
Application Fields
It is suitable for bonding of all thermal resistant materials such as metal, glass, plastic, wood and textiles.
- High-strength splicing (overlap splice)
- Friction liners for clutches
- Recommended for bonding of very rough materials due to its high thickness
Product Construction
| Adhesive Type | nitrile rubber / phenolic resin |
| Backing material | none |
| Color | amber |
| Liner Type | glassine |
| Total thickness | 10.63 mils
270 µm |
Properties / Performance Values
| Bonding strength (push-out) | 1740.45 lbs/in²
12 N/mm² |
| Bonding strength (dynamic shear) | 1740.45 lbs/in²
12 N/mm² |
Properties / Performance Values
| Bonding strength (push-out) | 1740.45 lbs/in²
12 N/mm² |
| Bonding strength (dynamic shear) | 1740.45 lbs/in²
12 N/mm² |
Additional Info
Processing:
1.Pre-lamination:
tesa HAF® 8400 is laminated before curing. For this process we recommend a temperature between 120 °C/248° F and 140 °C/284 °F.
2. Bonding:
The bonding conditions temperature, pressure and time depend on the application. Following parameters can be regarded as a guideline:
Splicing application:
To reach maximum bonding strength surfaces should be clean and dry. Storage conditions according to tesa HAF® shelf life concept.
1.Pre-lamination:
tesa HAF® 8400 is laminated before curing. For this process we recommend a temperature between 120 °C/248° F and 140 °C/284 °F.
2. Bonding:
The bonding conditions temperature, pressure and time depend on the application. Following parameters can be regarded as a guideline:
Splicing application:
- Temperature: 120 – 220 °C (248-428 °F)
- Pressure: > 2 bar
- Time: 15 – 90 s.
- Temperature: 180 – 230 °C (356-446 °F)
- Pressure: > 6 - 10 bar
- Time: 3 min – 30 min
To reach maximum bonding strength surfaces should be clean and dry. Storage conditions according to tesa HAF® shelf life concept.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.
Downloads
Download the files below for more technical details and information on this product.
![[en-en] tesa_HAF-amber_dr_001](/en-us/files/images/202402/2/medium-11173882,11173882_padded1x1_18.webp "tesa_HAF-amber_dr_001")
![[en-en] tesa_HAF-black_dr_001](/en-us/files/images/202402/2/medium-11173881,11173881_padded1x1_18.webp "tesa_HAF-black_dr_001")