tesa HAF® 9405

Double-sided reactive heat activated film

tesa-haf-8401-200-amber-reactive-mounting-tape-brown-084010001500-pr
Product description

tesa HAF® 9405 is a reactive heat activated film based on phenolic resin and nitrile rubber. This amber double sided tape has no backing. It is protected by a strong paper liner and can easily be slit and die cut.
At room temperature tesa HAF® 9405 is not tacky. It is activated by heat and starts to become tacky at 90°C for pre-lamination. In a second application step heat and pressure is applied over a certain period of time.
After curing tesa HAF® 9405 reaches:

1 Very high bonding strength
1 High temperature resistance of up to 350°C
1 Excellent chemical resistance
1 Resistance against oil and solvents
1 Bonds remain flexible and elastic

Product details and specifications

Application Fields

It is suitable for bonding of all thermal resistant materials such as metal, glass, plastic, wood and textiles.

1 Friction linings for clutch discs
1 Friction linings for synchronizer rings
1 Brake shims

Product Construction

Backing material none
Color amber
Total thickness 30 µm
Type of adhesive nitrile rubber / phenolic resin
Type of liner glassine

Properties / Performance Values

Bonding strength (dynamic shear) 12 N/mm²
Bonding strength (push-out) 12 N/mm²

Additional Info
Processing:
1. Pre-lamination:
tesa HAF® 9405 is laminated to the first substrate before curing. For this process we recommend a temperature between 90°C and 140°C.

2. Bonding:
The bonding conditions temperature, pressure and time depend on the application. Following parameters can be regarded as a guideline:

Friction linings for clutch discs:

1 Temperature: 180 – 230°C
1 Pressure: > 6 bar
1 Time: 3 min
3. Tempering (optional)
To reach the maximum bonding strength the bonded parts can be tempered at 180 - 230°C for 30 - 60 min without pressure.

Bonding strength values were obtained under standard laboratory conditions. Value is guaranteed clearance limit checked with each production batch (Material: Etched aluminium test specimen / Bonding conditions: Temp. = 120°C; p = 10 bar; t = 8 min)

To reach maximum bonding strength surfaces should be clean and dry. Storage conditions according to tesa HAF® shelf life concept.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.
Downloads

Download the files below for more technical details and information on this product.

Product information_tesa HAF® 09405_en-SG 65.7 kB