tesa® 75815
150μm d/s Chemical resistant acrylic foam tape
Product description
tesa® 75815 is a double-sided black tape. It is equipped with a high shock absorbing and chemical resistant adhesive.
Special features:
- Thickness: 150μm
- Excellent chemical resistance
- Very high shock performance
- Good wettability
- High sealing ability with superior waterproof (IPX8)
Product details and specifications
Application Fields
- Demanding touch panel, lens or screen mounting applications with high requirements for chemical and impact resistance
- Component mounting with high requirements for chemical and impact resistanc
- Mounting of 3D or ultra slim bezel designs
- Mounting of waterproof designs
| Backing material | none |
|---|---|
| Color | black |
| Colour of liner | transparent |
| Thickness of liner | 50 µm |
| Total thickness | 150 |
| Type of adhesive | acrylic |
| Type of liner | PET |
| Weight of liner | 72 g/m² |
| Ageing resistance (UV) | very good |
|---|
| Adhesion to PC (initial) | 9.5 N/cm |
|---|---|
| Adhesion to PC (after 3 days) | 16.5 N/cm |
| Adhesion to Steel (initial) | 8.5 N/cm |
| Adhesion to Steel (after 3 days) | 9.5 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.