tesa® 6917
Filmic double-sided bag sealing tape with differential adhesive
Product description
tesa® 6917 has been designed for re-sealable filmic bags. It consists of a transparent double-sided PP-film with a differential adhesive system. The product can easily be cut with the hot wire systems of common bag machine producers.
Due to different adhesion values on each side, tesa® 6917 offers good removability on the covered adhesive side.
tesa® 6917 comes with fingerlift (extended liner) for conveniant liner removal.
Due to different adhesion values on each side, tesa® 6917 offers good removability on the covered adhesive side.
tesa® 6917 comes with fingerlift (extended liner) for conveniant liner removal.
Application Fields
- Reopenable closure system for filmic bags
- Removable emblems or profiles
1 / 2
2 / 2
Product Construction
Type of adhesive | tackified acrylic, acrylic, advanced acrylic, modified acrylic |
Type of liner | PP |
Colour of liner | red, transparent |
Total thickness | 90 µm |
Thickness of liner | 80 µm |
Backing material | PP film |
Color | transparent, optically clear |
Properties / Performance Values
Elongation at break | 150 % |
Static shear resistance at 23°C | good |
Chemical resistance | good |
Humidity resistance | very good |
Tack | good |
Ageing resistance (UV) | very good |
Static shear resistance at 40°C | good |
Temperature resistance long term | 80 °C |
Softener resistance | medium, good |
Temperature resistance short term | 120 °C |
Adhesion to Values
Adhesion to PC (covered side, initial) | 4 N/cm |
Adhesion to PET (covered side, after 14 days) | 4.7 N/cm |
Adhesion to Steel (initial) | 8.2 N/cm |
Adhesion to PE (initial) | 3.9 N/cm |
Adhesion to PC (after 14 days) | 11 N/cm |
Adhesion to PS (after 14 days) | 10 N/cm |
Adhesion to Aluminium (covered side, initial) | 3.5 N/cm |
Adhesion to PS (covered side, initial) | 3.8 N/cm |
Adhesion to PE (covered side, after 14 days) | 2.3 N/cm |
Adhesion to ABS (initial) | 6.9 N/cm |
Adhesion to ABS (after 14 days) | 10.1 N/cm |
Adhesion to PP (after 14 days) | 6.9 N/cm |
Adhesion to PVC (covered side, initial) | 4 N/cm |
Adhesion to PET (after 14 days) | 9.3 N/cm |
Adhesion to Aluminium (after 14 days) | 10.2 N/cm |
Adhesion to ABS (covered side, after 14 days) | 6 N/cm |
Adhesion to PP (covered side, initial) | 1.9 N/cm |
Adhesion to PC (initial) | 9 N/cm |
Adhesion to PVC (initial) | 6.5 N/cm |
Adhesion to PE (covered side, initial) | 1.6 N/cm |
Adhesion to Steel (covered side, after 14 days) | 4.1 N/cm |
Adhesion to PET (covered side, initial) | 3.1 N/cm |
Adhesion to PE (after 14 days) | 4.1 N/cm |
Adhesion to PS (initial) | 7.9 N/cm |
Adhesion to ABS (covered side, initial) | 4.2 N/cm |
Adhesion to PET (initial) | 6.6 N/cm |
Adhesion to Alu (covered side, after 14 days) | 4.7 N/cm |
Adhesion to PC (covered side, after 14 days) | 6.8 N/cm |
Adhesion to Aluminium (initial) | 7.7 N/cm |
Adhesion to PS (covered side, after 14 days) | 5.6 N/cm |
Adhesion to PVC (covered side, after 14 days) | 7 N/cm |
Adhesion to PP (initial) | 3.8 N/cm |
Adhesion to Steel (after 14 days) | 11.4 N/cm |
Adhesion to Steel (covered side, initial) | 4.5 N/cm |
Adhesion to PVC (after 14 days) | 11 N/cm |
Adhesion to PP (covered side, after 14 days) | 2.6 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.