Product Construction
| Backing material | non-woven |
| Color | translucent |
| Color of liner | red |
| Thickness of liner | 80 µm |
| Total thickness | 250 µm |
| Type of adhesive | type: tackified acrylic |
| Type of liner | type: PE |
| Weight of liner | 92 g/m² |
tesa® 4914
Product Features
- Asymmetrical product design with superior adhesion on liner-covered side
- Excellent performance on rough surfaces like leather and textiles
- Reliable bond, even to low surface energy materials
Product details and specifications
Product Features
- Asymmetrical product design with superior adhesion on liner-covered side
- Excellent performance on rough surfaces like leather and textiles
- Reliable bond, even to low surface energy materials
- Low VOC according to VDA278 analysis
- Flame retardant according to FAR/JAR/CS 25.853(a) Appendix F part I (a)(1)(ii)
Product Construction
| Backing material | non-woven |
| Color | translucent |
| Color of liner | red |
| Thickness of liner | 80 µm |
| Total thickness | 250 µm |
| Type of adhesive | type: tackified acrylic |
| Type of liner | type: PE |
| Weight of liner | 92 g/m² |
Properties / Performance Values
| Elongation at break | 3 % |
| Tensile strength | 8 N/cm |
| Softener resistance | good |
| Temperature resistance short term | 140 °C |
| Static shear resistance | low |
| Ageing resistance (UV) | good |
| Humidity resistance | good |
| Tack | good |
| Chemical resistance | good |
| Temperature resistance min. | -40 °C |
| Static shear resistance at 40°C | low |
| Temperature resistance long term | 80 °C |
| Static shear resistance at 23°C | low |
Properties / Performance Values
| Elongation at break | 3 % |
| Tensile strength | 8 N/cm |
| Softener resistance | good |
| Temperature resistance short term | 140 °C |
| Static shear resistance | low |
| Ageing resistance (UV) | good |
| Humidity resistance | good |
| Tack | good |
| Chemical resistance | good |
| Temperature resistance min. | -40 °C |
| Static shear resistance at 40°C | low |
| Temperature resistance long term | 80 °C |
| Static shear resistance at 23°C | low |
Adhesion to Values
| Adhesion to ABS (initial) | 5.6 N/cm |
| Adhesion to ABS (after 14 days) | 7.7 N/cm |
| Adhesion to ABS (covered side, after 14 days) | 7.6 N/cm |
| Adhesion to ABS (covered side, initial) | 7.6 N/cm |
| Adhesion to Aluminium (initial) | 5.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 6.3 N/cm |
| Adhesion to Aluminium (covered side, after 14 days) | 8 N/cm |
| Adhesion to Aluminium (covered side, initial) | 7.8 N/cm |
| Adhesion to PC (initial) | 5.8 N/cm |
| Adhesion to PC (after 14 days) | 7.4 N/cm |
| Adhesion to PC (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PC (covered side, initial) | 8.1 N/cm |
| Adhesion to PE (initial) | 3.2 N/cm |
| Adhesion to PE (after 14 days) | 3.4 N/cm |
| Adhesion to PE (covered side, after 14 days) | 5.3 N/cm |
| Adhesion to PE (covered side, initial) | 4.2 N/cm |
| Adhesion to PET (initial) | 4.8 N/cm |
| Adhesion to PET (after 14 days) | 6.2 N/cm |
| Adhesion to PET (covered side, after 14 days) | 7.9 N/cm |
| Adhesion to PET (covered side, initial) | 7.8 N/cm |
| Adhesion to PP (initial) | 4.6 N/cm |
| Adhesion to PP (after 14 days) | 4.4 N/cm |
| Adhesion to PP (covered side, initial) | 5.6 N/cm |
| Adhesion to PP (covered side, after 14 days) | 6.5 N/cm |
| Adhesion to PS (initial) | 5.8 N/cm |
| Adhesion to PS (after 14 days) | 7.4 N/cm |
| Adhesion to PS (covered side, initial) | 8.1 N/cm |
| Adhesion to PS (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PVC (initial) | 4.8 N/cm |
| Adhesion to PVC (after 14 days) | 7.7 N/cm |
| Adhesion to PVC (covered side, after 14 days) | 7.8 N/cm |
| Adhesion to PVC (covered side, initial) | 7.8 N/cm |
| Adhesion to Steel (initial) | 7 N/cm |
| Adhesion to Steel (after 14 days) | 7.8 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 9.3 N/cm |
| Adhesion to Steel (covered side, initial) | 8.2 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 5.6 N/cm |
| Adhesion to ABS (after 14 days) | 7.7 N/cm |
| Adhesion to ABS (covered side, after 14 days) | 7.6 N/cm |
| Adhesion to ABS (covered side, initial) | 7.6 N/cm |
| Adhesion to Aluminium (initial) | 5.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 6.3 N/cm |
| Adhesion to Aluminium (covered side, after 14 days) | 8 N/cm |
| Adhesion to Aluminium (covered side, initial) | 7.8 N/cm |
| Adhesion to PC (initial) | 5.8 N/cm |
| Adhesion to PC (after 14 days) | 7.4 N/cm |
| Adhesion to PC (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PC (covered side, initial) | 8.1 N/cm |
| Adhesion to PE (initial) | 3.2 N/cm |
| Adhesion to PE (after 14 days) | 3.4 N/cm |
| Adhesion to PE (covered side, after 14 days) | 5.3 N/cm |
| Adhesion to PE (covered side, initial) | 4.2 N/cm |
| Adhesion to PET (initial) | 4.8 N/cm |
| Adhesion to PET (after 14 days) | 6.2 N/cm |
| Adhesion to PET (covered side, after 14 days) | 7.9 N/cm |
| Adhesion to PET (covered side, initial) | 7.8 N/cm |
| Adhesion to PP (initial) | 4.6 N/cm |
| Adhesion to PP (after 14 days) | 4.4 N/cm |
| Adhesion to PP (covered side, initial) | 5.6 N/cm |
| Adhesion to PP (covered side, after 14 days) | 6.5 N/cm |
| Adhesion to PS (initial) | 5.8 N/cm |
| Adhesion to PS (after 14 days) | 7.4 N/cm |
| Adhesion to PS (covered side, initial) | 8.1 N/cm |
| Adhesion to PS (covered side, after 14 days) | 8.2 N/cm |
| Adhesion to PVC (initial) | 4.8 N/cm |
| Adhesion to PVC (after 14 days) | 7.7 N/cm |
| Adhesion to PVC (covered side, after 14 days) | 7.8 N/cm |
| Adhesion to PVC (covered side, initial) | 7.8 N/cm |
| Adhesion to Steel (initial) | 7 N/cm |
| Adhesion to Steel (after 14 days) | 7.8 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 9.3 N/cm |
| Adhesion to Steel (covered side, initial) | 8.2 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.