Propriétés techniques
Backing material | non-woven |
Color | translucent |
Color of liner | brown |
Thickness of liner | 71 µm |
Total thickness | 100 µm |
Type of adhesive | type: tackified acrylic |
Type of liner | type: paper |
Adhésif double face non tissé
tesa® 4959 est un adhésif de fixation et de raccord double face composé d'un support non tissé recouvert d'une masse adhésive acrylique avec un tack élevé et une forte résistance au cisaillement. Le produit est résistant aux UV et au vieillissement ainsi qu'aux plastifiants.
Backing material | non-woven |
Color | translucent |
Color of liner | brown |
Thickness of liner | 71 µm |
Total thickness | 100 µm |
Type of adhesive | type: tackified acrylic |
Type of liner | type: paper |
Backing material | non-woven |
Color | translucent |
Color of liner | brown |
Thickness of liner | 71 µm |
Total thickness | 100 µm |
Type of adhesive | type: tackified acrylic |
Type of liner | type: paper |
Elongation at break | 2 % |
Tensile strength | 8 N/cm |
Tack | very good |
Temperature resistance min. | -40 °C |
Static shear resistance at 40°C | medium |
Ageing resistance (UV) | very good |
Temperature resistance long term | 80 °C |
Chemical resistance | good |
Static shear resistance at 23°C | good |
Temperature resistance short term | 200 °C |
Humidity resistance | very good |
Elongation at break | 2 % |
Tensile strength | 8 N/cm |
Tack | very good |
Temperature resistance min. | -40 °C |
Static shear resistance at 40°C | medium |
Ageing resistance (UV) | very good |
Temperature resistance long term | 80 °C |
Chemical resistance | good |
Static shear resistance at 23°C | good |
Temperature resistance short term | 200 °C |
Humidity resistance | very good |
Adhesion to ABS (initial) | 7.5 N/cm |
Adhesion to ABS (after 14 days) | 9 N/cm |
Adhesion to Aluminium (initial) | 7.5 N/cm |
Adhesion to Aluminium (after 14 days) | 8 N/cm |
Adhesion to PC (initial) | 9.5 N/cm |
Adhesion to PC (after 14 days) | 14 N/cm |
Adhesion to PE (initial) | 4 N/cm |
Adhesion to PE (after 14 days) | 4.5 N/cm |
Adhesion to PET (initial) | 7 N/cm |
Adhesion to PET (after 14 days) | 7.5 N/cm |
Adhesion to PP (initial) | 5.5 N/cm |
Adhesion to PP (after 14 days) | 6.5 N/cm |
Adhesion to PS (initial) | 8.5 N/cm |
Adhesion to PS (after 14 days) | 9 N/cm |
Adhesion to PVC (initial) | 6.5 N/cm |
Adhesion to PVC (after 14 days) | 14 N/cm |
Adhesion to Steel (initial) | 8 N/cm |
Adhesion to Steel (after 14 days) | 8.5 N/cm |
Adhesion to ABS (initial) | 7.5 N/cm |
Adhesion to ABS (after 14 days) | 9 N/cm |
Adhesion to Aluminium (initial) | 7.5 N/cm |
Adhesion to Aluminium (after 14 days) | 8 N/cm |
Adhesion to PC (initial) | 9.5 N/cm |
Adhesion to PC (after 14 days) | 14 N/cm |
Adhesion to PE (initial) | 4 N/cm |
Adhesion to PE (after 14 days) | 4.5 N/cm |
Adhesion to PET (initial) | 7 N/cm |
Adhesion to PET (after 14 days) | 7.5 N/cm |
Adhesion to PP (initial) | 5.5 N/cm |
Adhesion to PP (after 14 days) | 6.5 N/cm |
Adhesion to PS (initial) | 8.5 N/cm |
Adhesion to PS (after 14 days) | 9 N/cm |
Adhesion to PVC (initial) | 6.5 N/cm |
Adhesion to PVC (after 14 days) | 14 N/cm |
Adhesion to Steel (initial) | 8 N/cm |
Adhesion to Steel (after 14 days) | 8.5 N/cm |