tesa® 62935
1000μm double-sided PE foam tape
Product description
tesa® 62935 is a double-sided PE foam tape for constructive mounting applications. It consists of a high quality PE foam offering a high internal strength and is equipped with a tackified acrylic adhesive.
Product benefits:
- Versatile adhesive for high immediate adhesion on numerous substrates
- High ultimate adhesion level for a secure bonding performance
- Fully outdoor suitable: UV, water and ageing resistant
- Compensates for differing thermal expansion of dissimilar materials
- High immediate bonding strength even at low bonding pressure
- Very good cold shock absorbtion
Product details and specifications
Application Fields
Example mounting applications include but are not limited to:
- Mirrors and coloured glass panels
- Decorative aluminium cover screens on brown goods
- Doorhandles in kitchen furniture
- Moulded plastic parts
Product Construction
| Backing material | PE foam |
|---|---|
| Colour | black/white |
| Total thickness | 1,000 µm |
| Type of adhesive | tackified acrylic |
Product Construction
| Backing material | PE foam |
|---|---|
| Colour | black/white |
| Total thickness | 1,000 µm |
| Type of adhesive | tackified acrylic |
Properties / Performance Values
| Elongation at break | 345 % |
|---|---|
| Tensile strength | 12 N/cm |
| Ageing resistance (UV) | good |
| Humidity resistance | very good |
| Tack | good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term duration | 80 °C |
| Temperature resistance short term duration | 80 °C |
| Softener resistance | medium |
| Static shear resistance at 40°C | good |
Properties / Performance Values
| Elongation at break | 345 % |
|---|---|
| Tensile strength | 12 N/cm |
| Ageing resistance (UV) | good |
| Humidity resistance | very good |
| Tack | good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term duration | 80 °C |
| Temperature resistance short term duration | 80 °C |
| Softener resistance | medium |
| Static shear resistance at 40°C | good |
Adhesion to Values
| Adhesion to Aluminium (initial) | 17 N/cm |
|---|---|
| Adhesion to Aluminium (after 14 days) | 17 N/cm |
| Adhesion to PE (initial) | 2.7 N/cm |
| Adhesion to PE (after 14 days) | 3 N/cm |
| Adhesion to PET (initial) | 12.5 N/cm |
| Adhesion to PET (after 14 days) | 17 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 6 N/cm |
| Adhesion to PVC (initial) | 8 N/cm |
| Adhesion to PVC (after 14 days) | 17 N/cm |
| Adhesion to Steel (initial) | 17 N/cm |
| Adhesion to Steel (after 14 days) | 17 N/cm |
Adhesion to Values
| Adhesion to Aluminium (initial) | 17 N/cm |
|---|---|
| Adhesion to Aluminium (after 14 days) | 17 N/cm |
| Adhesion to PE (initial) | 2.7 N/cm |
| Adhesion to PE (after 14 days) | 3 N/cm |
| Adhesion to PET (initial) | 12.5 N/cm |
| Adhesion to PET (after 14 days) | 17 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 6 N/cm |
| Adhesion to PVC (initial) | 8 N/cm |
| Adhesion to PVC (after 14 days) | 17 N/cm |
| Adhesion to Steel (initial) | 17 N/cm |
| Adhesion to Steel (after 14 days) | 17 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.