Liner variants:
PV0 brown glassine paper (71µm; 82g/m²)
PV6 red MOPP-film (80µm; 72g/m²)
PV0 brown glassine paper (71µm; 82g/m²)
PV6 red MOPP-film (80µm; 72g/m²)
Double-sided all-round filmic tape
tesa® 4928 is a transparent double-sided self-adhesive tape consisting of a PET backing and a modified acrylic adhesive.
tesa® 4928 features:
| Backing material | PET film |
|---|---|
| Colour | transparent |
| Total thickness | 125 µm |
| Type of adhesive | tackified acrylic |
| Backing material | PET film |
|---|---|
| Colour | transparent |
| Total thickness | 125 µm |
| Type of adhesive | tackified acrylic |
| Elongation at break | 50 % |
|---|---|
| Tensile strength | 20 N/cm |
| Static shear resistance at 23°C | good |
| Chemical resistance | good |
| Temperature resistance long term duration | 100 °C |
| Tack | very good |
| Static shear resistance at 40°C | good |
| Softener resistance | good |
| Humidity resistance | very good |
| Ageing resistance (UV) | very good |
| Temperature resistance short term duration | 200 °C |
| Elongation at break | 50 % |
|---|---|
| Tensile strength | 20 N/cm |
| Static shear resistance at 23°C | good |
| Chemical resistance | good |
| Temperature resistance long term duration | 100 °C |
| Tack | very good |
| Static shear resistance at 40°C | good |
| Softener resistance | good |
| Humidity resistance | very good |
| Ageing resistance (UV) | very good |
| Temperature resistance short term duration | 200 °C |
| Adhesion to ABS (initial) | 8.2 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 9.7 N/cm |
| Adhesion to Aluminium (initial) | 8.1 N/cm |
| Adhesion to Aluminium (after 14 days) | 11.1 N/cm |
| Adhesion to PC (initial) | 10.3 N/cm |
| Adhesion to PC (after 14 days) | 11.5 N/cm |
| Adhesion to PE (initial) | 4.9 N/cm |
| Adhesion to PE (after 14 days) | 5.4 N/cm |
| Adhesion to PET (initial) | 7.4 N/cm |
| Adhesion to PET (after 14 days) | 8.7 N/cm |
| Adhesion to PP (initial) | 4.8 N/cm |
| Adhesion to PP (after 14 days) | 6.4 N/cm |
| Adhesion to PS (initial) | 8.8 N/cm |
| Adhesion to PS (after 14 days) | 9.4 N/cm |
| Adhesion to PVC (initial) | 7.2 N/cm |
| Adhesion to PVC (after 14 days) | 10.1 N/cm |
| Adhesion to Steel (initial) | 11.2 N/cm |
| Adhesion to Steel (after 14 days) | 12.8 N/cm |
| Adhesion to ABS (initial) | 8.2 N/cm |
|---|---|
| Adhesion to ABS (after 14 days) | 9.7 N/cm |
| Adhesion to Aluminium (initial) | 8.1 N/cm |
| Adhesion to Aluminium (after 14 days) | 11.1 N/cm |
| Adhesion to PC (initial) | 10.3 N/cm |
| Adhesion to PC (after 14 days) | 11.5 N/cm |
| Adhesion to PE (initial) | 4.9 N/cm |
| Adhesion to PE (after 14 days) | 5.4 N/cm |
| Adhesion to PET (initial) | 7.4 N/cm |
| Adhesion to PET (after 14 days) | 8.7 N/cm |
| Adhesion to PP (initial) | 4.8 N/cm |
| Adhesion to PP (after 14 days) | 6.4 N/cm |
| Adhesion to PS (initial) | 8.8 N/cm |
| Adhesion to PS (after 14 days) | 9.4 N/cm |
| Adhesion to PVC (initial) | 7.2 N/cm |
| Adhesion to PVC (after 14 days) | 10.1 N/cm |
| Adhesion to Steel (initial) | 11.2 N/cm |
| Adhesion to Steel (after 14 days) | 12.8 N/cm |
Download the files below for more technical details and information on this product.