Product Construction
Backing material | PE foam |
Colour | black/white |
Total thickness | 800 µm |
Type of adhesive | type: tackified acrylic |
800µm double-sided foam tape
tesa® 62394 is a double-sided foam tape consisting an adaptable PE-foam substrate and a modified acrylate adhesive mass. This combination is highly adhesive and can be applied to many different surfaces. This foam tape is resistant to ageing, moisture and temperatures of up to 80 °C. It is also highly resistant to sudden chills, and is able to compensate for the thermal expansion of various materials.
Backing material | PE foam |
Colour | black/white |
Total thickness | 800 µm |
Type of adhesive | type: tackified acrylic |
Backing material | PE foam |
Colour | black/white |
Total thickness | 800 µm |
Type of adhesive | type: tackified acrylic |
Elongation at break | 250 % |
Tensile strength | 8 N/cm |
Softener resistance | medium, good |
Humidity resistance | very good |
Static shear resistance at 23°C | good, medium |
Static shear resistance at 40°C | good, medium |
Ageing resistance (UV) | good |
Temperature resistance short term duration | 80 °C |
Temperature resistance long term duration | 80 °C |
Tack | good, medium |
Elongation at break | 250 % |
Tensile strength | 8 N/cm |
Softener resistance | medium, good |
Humidity resistance | very good |
Static shear resistance at 23°C | good, medium |
Static shear resistance at 40°C | good, medium |
Ageing resistance (UV) | good |
Temperature resistance short term duration | 80 °C |
Temperature resistance long term duration | 80 °C |
Tack | good, medium |
Adhesion to ABS (initial) | 17 N/cm |
Adhesion to ABS (after 14 days) | 17 N/cm |
Adhesion to Aluminium (initial) | 17 N/cm |
Adhesion to Aluminium (after 14 days) | 17 N/cm |
Adhesion to PC (initial) | 15 N/cm |
Adhesion to PC (after 14 days) | 17 N/cm |
Adhesion to PE (initial) | 2.7 N/cm |
Adhesion to PE (after 14 days) | 2.8 N/cm |
Adhesion to PET (initial) | 12.5 N/cm |
Adhesion to PET (after 14 days) | 17 N/cm |
Adhesion to PP (initial) | 2.8 N/cm |
Adhesion to PP (after 14 days) | 5.5 N/cm |
Adhesion to PS (initial) | 15 N/cm |
Adhesion to PS (after 14 days) | 17 N/cm |
Adhesion to PVC (initial) | 17 N/cm |
Adhesion to PVC (after 14 days) | 17 N/cm |
Adhesion to Steel (initial) | 17 N/cm |
Adhesion to Steel (after 14 days) | 17 N/cm |
Adhesion to ABS (initial) | 17 N/cm |
Adhesion to ABS (after 14 days) | 17 N/cm |
Adhesion to Aluminium (initial) | 17 N/cm |
Adhesion to Aluminium (after 14 days) | 17 N/cm |
Adhesion to PC (initial) | 15 N/cm |
Adhesion to PC (after 14 days) | 17 N/cm |
Adhesion to PE (initial) | 2.7 N/cm |
Adhesion to PE (after 14 days) | 2.8 N/cm |
Adhesion to PET (initial) | 12.5 N/cm |
Adhesion to PET (after 14 days) | 17 N/cm |
Adhesion to PP (initial) | 2.8 N/cm |
Adhesion to PP (after 14 days) | 5.5 N/cm |
Adhesion to PS (initial) | 15 N/cm |
Adhesion to PS (after 14 days) | 17 N/cm |
Adhesion to PVC (initial) | 17 N/cm |
Adhesion to PVC (after 14 days) | 17 N/cm |
Adhesion to Steel (initial) | 17 N/cm |
Adhesion to Steel (after 14 days) | 17 N/cm |