tesa HAF® 8451
200µm amber reactive HAF mounting tape
Product descriptiontesa HAF® 8451 is a reactive heat activated film based on phenolic resin and nitrile rubber. It is especially designed for applications that require high resistance against shock, e.g. in case of dropping. This amber double sided tape has no backing. It is protected by s strong paper liner.
tesa HAF® 8451 is free of halogen and compliant with current ROHS standards.
At room temperature tesa HAF® 8451 is not tacky. It is activated by heat and pressure applied during the assembly process.
- Reliable and ageing resistant bonds
- Extremely high performance, even on small bonding areas and thin design gaps
- Excellent shock resistance, especially at low temperatures
- Very low oozing ratio
- Suitable for long-term applications that are exposed to heavy stress
- Bonds remain elastic
Main applicationstesa HAF®8451 is especially recommended for bonding of metal components to various plastic or metal surfaces, e.g. SUS or AL to PMMA, PC or ABS.
- Constructive bonding inside electronic devices
- Button fixation
- Camera lens and bezel mounting
- Bonding of decorative metal components
Shelf life time < 25°C
Type of adhesive
nitrile rubber / phenolic resin
Shelf life time < 15°C
Type of liner
Shelf life time < 5°C
Additional InfoTechnical Recommendations:
tesa HAF® 8451 is not self adhesive. It is activated by pressure and heat over a certain interval. The following values are recommendations for bond line parameters to start with.
During pre-lamination, the adhesive tape is laminated onto the metal substrate. This step does not affect the shelf life time of the adhesive tape. Pre-laminated components can be stored over the same period of time as the adhesive tape.
- Temperature¹ 70 – 120 °C
- Pressure² 2 – 6 bar
- Time 1.5 – 3.0 s.
Remove the liner from tape after pre-lamination step. Combine the plastic onto the metal component. Apply sufficient temperature through metal to the plastic component while applying pressure for the bonding time to reach a sufficient bonding strength.
- Temperature¹ 160 – 200 °C
- Pressure² 2 – 10 bar
- Time 3 – 10 s.
¹ ‘Pre-lamination’ and ‘Bonding’ temperature refer to the data that is measured in the bond line.
² ‘Pre-lamination’ and ‘Bonding’ pressure refer to the force that is transformed from jig surface directly to the bonding area.<.
Bonding strength values were obtained under standard laboratory conditions. (Material: AL & AL test specimen / Bonding conditions: Temperature = 180 °C; Pressure = 10 bar; Time = 7 sec).br/>
Storage conditions according to tesa HAF® shelf life concept.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.