tesa® 60933
Double-sided non-woven tape
Product description
tesa® 60933 is a double-sided tape consisting a non-woven backing and a tackified acrylic adhesive.
tesa® 60933 features especially:
- Good adhesion values on different substrates
Main applications
- Lamination of foam and felt
Technical properties
Backing material
non-woven
Color
translucent
Total thickness
80 µm
Type of adhesive
tackified acrylic
Type of liner
glassine
Colour of liner
white
Thickness of liner
66 µm
Weight of liner
82 g/m²
Adhesion properties
Adhesion to ABS (after 14 days)
7.5 N/cm
Adhesion to ABS (initial)
4.8 N/cm
Adhesion to Aluminium (after 14 days)
8.5 N/cm
Adhesion to Aluminium (initial)
4 N/cm
Adhesion to PC (after 14 days)
7.6 N/cm
Adhesion to PC (initial)
5.1 N/cm
Adhesion to PET (after 14 days)
5.2 N/cm
Adhesion to PET (initial)
3.5 N/cm
Adhesion to PP (after 14 days)
3.5 N/cm
Adhesion to PP (initial)
3.1 N/cm
Adhesion to Steel (after 14 days)
8.9 N/cm
Adhesion to Steel (initial)
5.4 N/cm
Rating properties
Temperature resistance short term
160 °C
Temperature resistance long term
80 °C
Tack
++
Ageing resistance (UV)
++
Humidity resistance
+
Resistance to chemicals
+
Softener resistance
o
Static shear resistance at 23°C
o
Static shear resistance at 40°C
-
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.