Product description
tesa® 4914 is a translucent double-sided self-adhesive tape consisting of a non-woven backing and a tackified acrylic adhesive with lower coating weight on the open side.
tesa® 4914 features especially:
- Open side: lower adhesion level
- Easier removal while tearing the bond apart from the original surface even after exposure to demanding environmental conditions
- Covered side: higher adhesion level
- Foamed adhesive coating with high initial tack
- Excellent performance on rough surfaces
Main applications
- Mounting of car roof linings in car production
- Lamination of foamed materials in combination with smooth materials on the open side
Technical properties
Backing material
non-woven
Color
translucent
Total thickness
250 µm
Type of adhesive
tackified acrylic
Elongation at break
3 %
Tensile strength
8 N/cm
Type of liner
PE
Colour of liner
red
Thickness of liner
80 µm
Weight of liner
92 g/m²
Adhesion properties
Adhesion to ABS (after 14 days)
7.7 N/cm
Adhesion to ABS (covered side, after 14 days)
7.6 N/cm
Adhesion to ABS (covered side, initial)
7.6 N/cm
Adhesion to ABS (initial)
5.6 N/cm
Adhesion to Alu (covered side, after 14 days)
8 N/cm
Adhesion to Aluminium (after 14 days)
6.3 N/cm
Adhesion to Aluminium (covered side, initial)
7.8 N/cm
Adhesion to Aluminium (initial)
5.2 N/cm
Adhesion to PC (after 14 days)
7.4 N/cm
Adhesion to PC (covered side, after 14 days)
8.2 N/cm
Adhesion to PC (covered side, initial)
8.1 N/cm
Adhesion to PC (initial)
5.8 N/cm
Adhesion to PE (after 14 days)
3.4 N/cm
Adhesion to PE (covered side, after 14 days)
5.3 N/cm
Adhesion to PE (covered side, initial)
4.2 N/cm
Adhesion to PE (initial)
3.2 N/cm
Adhesion to PET (after 14 days)
6.2 N/cm
Adhesion to PET (covered side, after 14 days)
7.9 N/cm
Adhesion to PET (covered side, initial)
7.8 N/cm
Adhesion to PET (initial)
4.8 N/cm
Adhesion to PP (after 14 days)
4.4 N/cm
Adhesion to PP (covered side, after 14 days)
6.5 N/cm
Adhesion to PP (covered side, initial)
5.6 N/cm
Adhesion to PP (initial)
4.6 N/cm
Adhesion to PS (after 14 days)
7.4 N/cm
Adhesion to PS (covered side, after 14 days)
8.2 N/cm
Adhesion to PS (covered side, initial)
8.1 N/cm
Adhesion to PS (initial)
5.8 N/cm
Adhesion to PVC (after 14 days)
7.7 N/cm
Adhesion to PVC (covered side, after 14 days)
7.8 N/cm
Adhesion to PVC (covered side, initial)
7.8 N/cm
Adhesion to PVC (initial)
4.8 N/cm
Adhesion to Steel (after 14 days)
7.8 N/cm
Adhesion to Steel (covered side, after 14 days)
9.3 N/cm
Adhesion to Steel (covered side, initial)
8.2 N/cm
Adhesion to Steel (initial)
7 N/cm
Rating properties
Temperature resistance short term
140 °C
Temperature resistance long term
80 °C
Tack
+
Ageing resistance (UV)
+
Humidity resistance
+
Resistance to chemicals
+
Softener resistance
+
Static shear resistance
-
Static shear resistance at 23°C
-
Static shear resistance at 40°C
-
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.